Antimony Trisulfide
|
|
|
Synonyms: Antimony Sulfide
|
|
|
Molecular
formula: Sb2S3
|
|
|
CAS
No.1345-04-6
|
|
|
|
H
.S code:2830.9020
|
|
|
Molecular
Weight: 339.68.
|
|
|
Melting
Point: 550 Centigrade
|
|
|
Boiling
Point:1080-1090Centigrade.
|
|
Hardness:HB2-2.5.Density:4.64g/cm3.
|
|
Vapor
pressure: 156Pa(500℃)
|
|
|
Volatility:
None
|
|
|
|
Relative
weight: 4.6(13℃)
|
|
|
Solubility
(water): 1.75mg/L(18℃)
|
|
|
Others:
soluble in acid hydrochloride
|
|
Appearance:
black powder or silver black little blocks.
|
About Antimony Trisulfide
Tint: According to its different particle sizes, manufacturing methods and production conditions, the formless antimony trisulfide is provided with different colors, such as gray, black, red, yellow, brown and purple, etc..
Fire Point: Antimony trisulfide is easy to be oxidized. Its fire point - the temperature when it begins self-heat and oxidation in the air depends on its particle size. When the particle size is 0.1mm, the fire point is 290 Centigrade; when the particle size is 0.2mm, the fire point is 340 Centigrade.
Solubility: Insoluble in water but soluble in hydrochloric acid. In addition, it can also dissolve in the hot concentrated sulfuric acid.
Appearance: There should not be any impurity that can be differentiated by eyes.
Enterprise Standard of Antimony Trisulfide Specification
Symbol
|
Application
|
Content
Min.(%)
|
Element Controlled (%)
|
MoistureMax.
|
Free Sulphu
Max.
|
Fineness
(mesh) >98%
|
Sb>
|
S>
|
As<
|
Pb<
|
Se<
|
UMATF95
|
Friction Materials
|
95
|
69
|
26
|
0.2
|
0.2
|
0.04
|
1%
|
0.07%
|
180(80µm)
|
UMATF90
|
90
|
64
|
25
|
0.3
|
0.2
|
0.04
|
1%
|
0.07%
|
180(80µm)
|
UMATGR85
|
Glass&Rubber
|
85
|
61
|
23
|
0.3
|
0.4
|
0.04
|
1%
|
0.08%
|
180(80µm)
|
UMATM70
|
Matches
|
70
|
50
|
20
|
0.3
|
0.4
|
0.04
|
1%
|
0.10%
|
180(80µm)
|
Packaging status: petroleum barrel (25kg), paper box (20、25kg),or as customer’s requirement.
What is Antimony Trisulfide used for?
Antimony Trisulfide(Sulfide) is widely used in the war industry including gunpowder, glass and rubber, match phosphorus, fireworks, toy dynamite, simulated cannonball and friction materials and so on as the additive or catalyst, anti-blushing agent and heat-stabilizer and also as the flame-retardant synergist replacing antimony oxide.