Automobile Industry Application PDCPD Material Auto Parts
PDCPD Products High Properties Test Reference
|
Content
|
Unit
|
Testing Method
|
Content
|
Unit
|
Testing Method
|
|
Tensile strength
|
47.5MPa
|
GB/T 1040.2-2006
|
Rockwell hardness
|
115
|
GB/T3398.2-2008
|
|
Tensile modulus
|
1900MPa
|
GB/T 1040.2-2006
|
Distortion temperature
|
110.5
|
GB/T1634.2-2004
|
|
Elongation at break
|
12.30%
|
GB/T 1040.2-2006
|
Density
|
1.03g/cm³
|
GB/T1033.1-2008
|
|
Compressive strength
|
60.8MPa
|
GB/T 1041-2008
|
Glass transition temperature
|
169℃
|
GB/T19466.2-2004
|
|
Bending strength
|
75.6MPa
|
GB/T9341-2008
|
Burning horizontally
|
HB40
|
GB/T2408-2008
|
|
Bending modulus of elasticity
|
2053MPa
|
GB/T9341-2008
|
Water Absorption
|
0.10%
|
GB/T1034-2008
|
|
Notched impact strength
of cantilever beam (23℃)
|
33.1
|
GB/T1843-2008
|
Automotive interior combustion
Performance (burning rate)
|
A-0
|
GB 8410-2006
|
|
Notched impact strength of
cantilever beam (-40℃)
|
12.8
|
GB/T1843-2008
|
Rockwell hardness
|
115
|
GB/T3398.2-2008
|
Ten Advantages of PDCPD Products Properties
1. Wide molding range: two-component, low-viscosity liquid resin injection molding, shape, runner, and pressure restrictions are small, can produce large, complex shapes, the wall thickness of the workpiece.
2. Equipment Investment: simple molding process, low pressure and temperature requirements, less investment in molding equipment, low mold costs, long service life of the mold, small amortization costs
3. Good balance of physical properties: excellent and balanced physical properties, especially the combination of high impact resistance and high rigidity, can get lightweight, high strength, rugged, and durable parts.
4. Temperature and corrosion resistance: outstanding resistance to temperature change, high temperature does not creep, low temperature does not cause brittle crack, can be used in -40 ~ 100 ℃ environment for a long time: excellent corrosion resistance, especially acid resistance, alkali resistance is outstanding.
5. High product precision: the product deformation is small, the size error is small, and the consistency of the workpiece is high; in general, the control of the size error of the workpiece can reach the GB/T1804-m level.
6. Excellent decorative properties: the surface of the molded parts is easy to form a dense oxide film with good adhesion to paint. It can also be plated, water transfer printing, and other surface decorative treatments.
7. Good designability: high degree of design freedom, can be pre-embedded, riveted, glued, self-tapping, and drilling, can be unequal thickness structure, sandwich structure, composite structure, etc.
8. High molding efficiency: short mold development cycle. Less production labor, high molding efficiency, product molding cycle is generally 3 ~ 5 min. can be configured with robot to achieve automated demolding, trimming, and so on.
9. Good Safety and environmental protection: no fiber and dust, no poison and pollution, less edge residue, recyclable and harmless reuse, reuse more ways, high added value.
10. Wide range of applications, design freedom, applied in various automobiles, engineering equipment, medical equipment, chemical equipment, entertainment facilities, military, civilian, and other fields. Excellent performance, PDCPD material process, green, lightweight, high strength, green, fast and economical industrial closure.