Nano Crystallized Glass Stone Panels is an inorganic artificial stone by with high temperature smelting. Main material is SIO2, a very hard and high glossy engineered stone than Quartz Stone. It is suitable for internal and external wall, floors, work tops, columns.
There are many colors we can supply:
1. Pure White Nano Crystallized Glass: CN-003
2. Calacatta Nano Crystallized Glass: CN-101, CN-102, CN-104
3. Statuario Nano Crystallized Glass: CN-103
4. Wood Vein Nano Crystallized Glass: WN-101, WN-102
5. Solid veins Nano Crystallized Glass with random patterns.
Finish:
|
Polished,
Bushhammered
|
Slab Size:
|
2800x1500mm,
2800x1600mm etc.
|
Tiles Size:
|
300x300, 300x600,
600x600, 600x1200mm etc.
|
Thickness:
|
18mm normal
thickness, 12mm, 20mm, 30mm special thickness
|
HS Code:
|
701690900
Crystallized Glass Slabs
7006000090 Crystallized Glass Countertops / Columns etc.
|
Application:
|
Interior and Exterior White Nano Crystal Glass Work tops
application:
Kitchen Countertops, Backsplash, Work Tops, Bench tops, Table Tops, Bathroom Shower Wall, Vanity tops;
Exterior and Interior White Nano Crystal Glass
Flooring Tiles;
Exterior and Interior White Nano Crystal Glass Wall Facade Tiles;
Exterior and Interior White Nano Crystal Glass Column Shafts;
|
Nano Crystallized Glass Stone Panels Test Report
|
|
|
|
|
|
|
|
Material
Name: Nanoglass CN-003
|
Center Ref No.:
WT2016B02N00620
|
|
Manufcacturer:
Enming Art Stone Co., Ltd.
|
Report Date: March
23th., 2016
|
|
|
|
|
|
|
|
|
No.
|
Test Items
|
Standard Index
|
Test Results
|
Individual
Conclusion
|
Test Standard
|
1
|
Specular Gloss
|
High
Class Products≥85
|
86
|
Pass
|
JC/T872-2000
|
2
|
Flexural Strength
|
|
71.5MPa
|
Pass
|
3
|
Mohs' Hardness
|
Grade 5 to Grade 6
|
Grade 6
|
Pass
|
4
|
Thermal Shock Resistance
|
No Crazing
|
No Crazing
|
Pass
|
5
|
Radionuclides(Class A)
|
Internal
Exposure Index
|
A
class:≤1.0
|
0.1
|
A Class
|
GB6566-2010
|
External Exposure Index
|
A
class:≤1.3
|
0.11
|
A Class
|
6
|
Water Absorption
|
-----------
|
0.003%
|
-----------
|
GB/T3810.3-2006
|
7
|
Apparent Relative Density
|
-----------
|
2.580%
|
-----------
|
8
|
Abrasion Resistance
|
-----------
|
1.1x10-3g/cm2
|
-----------
|
Refer
to SN/T0308-93
|
9
|
Point Impact
|
-----------
|
The
unit Showed no Cracks and Chips after 1kg steel ball droped from a height of
50cm
|
-----------
|
10
|
Compression Strength
|
-----------
|
505MPa
|
-----------
|
Refer
to JC/T262-93
|
11
|
Impact Toughness
|
-----------
|
3.5KJ/m2
|
-----------
|
Refer
to JC/T259-93
|
12
|
Linnear Thermal Expansion
|
-----------
|
8.8x10-6。C-1
|
-----------
|
Refer
to GB/T 3810.8-2006
|
13
|
High Tempture. Resistance
|
-----------
|
No
Cracking, Crazing, Blistering, No Color Differences
|
-----------
|
Refer to JC/T 908-2013
|
14
|
Load Test
|
-----------
|
No
Cracking (Residual deflection is 0.02mm)
|
-----------
|
15
|
Chemical Resistance
|
-----------
|
The
surface finish is unaffected
|
-----------
|
|
|
|
|
|
|
|
Test
by: National Research Center of Testing Techniques for Building Materials
|
|
Add:South Building,China Building
Material Center, Guan Zhuang, Chaoyang District, Beijing China.
|