MX-Zn-JG-01 Non-cyanide alkaline zinc plating brightening agent
MX-Zn-JG-01 brightening agent can be operated with iron anode, so with
such stability, it’s easy to manage and can be used over a wide range.
Features:
1. Due to the iron anode, it’s no need to
take the anode out during downtime.
2. With good leveling ability, the
thickness variation can be controlled to the minimum
limit.
3. The distinctive physical properties
allow it to be reprocessed, like, bending, rolling and clamping.
4. Easy to manage in terms of plating
solution’ composition, temperature and battery.
5. Stable corrosion resistance can be
acquired, if the passivation.
6. Is carried out by passivation agent with
no hexavalent chrome.
Using
method
|
Composition
|
Standard concentration
|
Best scope
|
|
Metallic zinc（g/L）
|
10
|
8-15
|
|
sodium hydroxide（g/L）
|
125
|
100-150
|
|
MX-Zn-JG-01A(ml/L)
|
12
|
10-15
|
|
MX-Zn-JG-01B(ml/L)
|
1.2
|
1-2
|
|
MX-Zn-JG-01C(ml/L)
|
5
|
3-7
|
|
MX-Zn-JG-01D(ml/L)
|
4
|
2-6
|
Supplement amount
MX-Zn-JG-01A(ml/L) 40-80ml/
Ka
MX-Zn-JG-01B(ml/L) 100-200ml/
Ka
MX-Zn-JG-01C(ml/L) 20-60ml/
Ka
MX-Zn-JG-01B(ml/L) added
in open cylinder： after processing