Feature
Avoid using primer bonding process
Good stability in the water-borne systems
It provides better adhesion to the substrate
Can extend the shelf life and stability of the resin
Moisture can reduce the absorption of the composite mold
The modified system is light in color, no bubbles after curing
Improves wet electrical properties, especially at low frequencies
Can improve the adhesion to the metal substrate to increase strength
Make textiles soft, smooth, breathable, waterproof and more flexible
The fabric has excellent softness, smoothness and other finishing effects
Improve the adhesion while maintaining the elongation at break of rubber to improve the shelf life of the formulation
Can significantly increase the strength of the friction material, long life, easy to sand collapse
Resin can achieve internal damage rather than the interfacial adhesion between the sealant layer and the substrate damage
Type
N-β- aminoethyl -γ- aminopropyl methyl dimethoxy silane
Typical properties
Appearance: Colorless to pale yellow liquid
Content: ≥97%
Flash point: 93℃
Boiling point: 256℃
Molecular weight: 206
CAS No.: 3069-29-2
Density: 0.965-0.975g/cm3
Refractive index: 1.430 ± 0.020
Structural formula: NH2(CH2)2NH(CH2)3SiCH3(OCH3)2
Recommended Consumption: 1% by weight of filler
Solubility: Dissolved in benzene, ethanol, propanol and other organic solvents, can be dissolved in water to produce an oily liquid after hydrolysis fused after placement
Application
-Textile industry
-Plastisol sealant
-Foundry Industry
-Polysulfide sealant(for glass, aluminum and steel)
-Added to the phenolic resin and epoxy molding compound
-Suitable resins include furan resins, phenol resins, RTV resins, trimer nitrile amine, D4, DMC, PA, PU, etc.
Storage and handling
Available in 25 kg/drum
Store products in tightly closed original containers at 5-40℃
Shelf life: 12 months from delivery date
According to non-dangerous goods transport