Description
As temperature resistance decorative non-stick coating, it could be used on outside of aluminum non-stick cookware. Please do complete applicability test for specific use.
Type
Silicone coating
Key features
-Eco-friendly and PFOA free
-Showing the effect of natural marble
-Easy application process, with bright color
-It’ s workable at 200℃, good chemical resistance
Typical properties
Product model： S-202A (Primer)
S-202B (Dot-1)
S-202C (Dot-2)
Recommended dosage： 10kg primer
0.5kg Dot-1: 0.5kg Dot-2
Appearance： Light brown (Primer)
Light yellow (Dot-1)
Black (Dot-2)
Solid content (%)： 45±1 (Primer)
40±1 (Dot-1)
39±1 (Dot-2)
Viscosity (cp)： 30~50 (Primer)
10~16 (Dot-1)
10~16 (Dot-2)
Density (g/ml)： 1.20±0.20 (Primer)
1.25±0.20 (Dot-1)
1.25±0.20 (Dot-2)
pH： 8~11 (Primer)
8~11 (Dot-1)
8~11 (Dot-2)
Gloss (60° glossimeter)： 45-55
Film thickness (μm)： 15-25
Hardness： >3H (ZHONGHUA pencil)
Adhesion (1mm*1mm)： Grade 1
Application
-Outside of tensile aluminum and die-casting fry pan, wok, soup pot, etc.
Storage and handling
-Available in 20 kg/ barrel or 30 kg/ barrel
-Store products in tightly closed original containers at 5-35℃
-Shelf life: 12 months from delivery date
-According to non-dangerous goods transport
How to use
1. Requirement on pre-treatment
-Firstly, apply high-temperature degreasing, then wash with 1%~3% NaOH solution (60℃) for more than 6 minutes, dry it after water rinsing.
-Blast with 80#~120# corundum to make the surface roughness reach 2.0μ~3.0μ, pay attention to sandblast evenly;
-Wash with 1%~3% NaOH solution(60℃) for more than 6 minutes, rinse with water.
-Wash with 1%~3% hydrochloric acid solution (60℃) for more than 6 minutes, rinse with water and dry.
2. Preparation of the coating
-Dispersion of coating: the coating must be fully dispersed before operation. Rolling the coating at the speed of 300rpm with rolling machine for 10mins at least.
-Coating filtration: filtrate the coating with screen (100mesh) before using.
3. Application
-The spraying environment should be dry, well-ventilated, no smoking and fire. We suggest using dedicated spray gun, elevated tank and curing oven.
-The air compressor should be degreased, dewatered and equipped with water oil separator before using.
-Adjust atomization and oil pump capacity of the spraying gun; make sure the unit is clean and flat.
-Leveling the coating at 150~180℃ after spraying, cure it at 280℃×10min. Keep the dry film thickness at the range of 15μm~25μm.
-In spraying process, keep stirring inside of the elevated tank, the size of spraying nozzle should be between 0.8mm~ 1.3mm, the pressure is about 3.5bar.
Non-stick Coating Type
↓ ↓ ↓ Please click product model for more informations
|
Model
|
Layer
|
Thickness
|
Curing temperature
|
Non stick property
|
Anti-corrosion
|
Abrasion resistant
|
|
Water based fluororesin non-stick coating
|
|
PF-600
|
2
|
25-40
|
380-400
|
A A A A A
|
A A A A
|
A A A
|
|
PF-601
|
2
|
25-35
|
380-400
|
A A A A
|
A A A A
|
A A A
|
|
PF-602
|
2
|
25-40
|
380-400
|
A A A A A
|
A A A A
|
A A A
|
|
PF-610
|
3
|
20-35
|
380-420
|
A A A A A
|
A A A A A
|
A A A
|
|
PF-611
|
3
|
20-35
|
380-420
|
A A A A A
|
A A A A A
|
A A A
|
|
PF-612
|
3
|
20-35
|
380-420
|
A A A A A
|
A A A A A
|
A A A
|
|
Water based ceramic non-stick coating
|
|
C-104
|
1
|
30-45
|
280-300
|
A A A A A
|
A A A A
|
A A A A A
|
|
C-105
|
1
|
30-45
|
280-300
|
A A A A A
|
A A A A
|
A A A A A
|
|
C-106
|
2
|
34-50
|
280-300
|
A A A A A
|
A A A A
|
A A A A A
|
|
C-107
|
1
|
12-20
|
250-280
|
A A A A A
|
A A A A
|
A A A A A
|
|
C-108
|
2
|
34-50
|
280-300
|
A A A A A
|
A A A A
|
A A A A A
|
|
C-109
|
2
|
34-50
|
280-300
|
A A A A A
|
A A A A
|
A A A A A
|
|
Silicone resin non-stick coating
|
|
S-200
|
1
|
15-20
|
280-300
|
A A A A
|
A A A A A
|
A A A A
|
|
S-201
|
1
|
15-20
|
280-300
|
A A A A
|
A A A A A
|
A A A A A
|
|
S-202
|
1
|
15-20
|
280-300
|
A A A A
|
A A A A A
|
A A A A
|