Description
Silicone resin non-stick coating S-200 is particularly designed for baking operation, and features extraordinarily glossy surface, outstanding stain resistance, non-stick performance and superior scratch resistance. The surface is easy to clean after baking operation. It has a very good operability, it is workable at 200℃, can be widely applied on the inside coating of iron bakeware.
Type
Solvent based silicone resin
Key features
-High-gloss
-Excellent heat resistant
-Excellent chemical resistance and abrasive resistance
-Excellent and lasting non-stick performance, easy to clean
Typical properties
Appearance: Yellowish clear liquid
Solid content (%): 35±1
Viscosity (cp): 400~800 Primer
Density (g/ml): 1.10
pH: 8-10
Color of the film surface: Black with metallic (Flat and smooth)
Curing temperature (℃): 280-300
Gloss (60° glossimeter): 10-20
Film thickness (μm): 15-20
Non-stick performance: >5 cycles (Fry eggs at 170±10℃)
Corrosion resistance: No blister (Boling 3% HAc for 1 hours)
Abrasion resistance 3KG/21cm2: No blister
Hardness (ZHONGHUA pencil): 3H-5H
Application
-Bakeware made of aluminum, stainless and carbon steel
Storage and handling
-Available in 20 kg/ barrel or 30 kg/ barrel
-Store products in tightly closed original containers at 5-40℃
-Shelf life: 9 months from delivery date
-According to non-dangerous goods transport
HOW TO USE
1. Requirement on pre-treatment
-Firstly, apply high-temperature degreasing, then wash with 1%~3% NaOH solution (60℃) for more than 6 minutes. Then dry it after water rinsing;
2. Preparation of the coating
-Dispersion of coating: the coating must be fully dispersed before operation by stirring;
-Viscosity adjustment: the viscosity could be adjusted according to different spray methods. Dilute with special thinner if the viscosity is over high;
-Coating filtration: filtrate the coating with screen (200-400 mesh) before using.
3. Application
-The spraying environment should be dry, well-ventilated, no smoking and fire;
-Use electrostatic spraying and dry out the workpieces at 100-150℃;
-Adjust atomization and oil pump capacity of spray gun. Make sure the unit it clean and level. Keep the thickness is within 15μm-20μm;
-Dry the workpieces at 280℃ for 5-10min.
Non-stick Coating Type
↓ ↓ ↓ Please click product model for more informations
|
Model
|
Layer
|
Thickness
|
Curing temperature
|
Non stick property
|
Anti-corrosion
|
Abrasion resistant
|
|
Water based fluororesin non-stick coating
|
|
PF-600
|
2
|
25-40
|
380-400
|
A A A A A
|
A A A A
|
A A A
|
|
PF-601
|
2
|
25-35
|
380-400
|
A A A A
|
A A A A
|
A A A
|
|
PF-602
|
2
|
25-40
|
380-400
|
A A A A A
|
A A A A
|
A A A
|
|
PF-610
|
3
|
20-35
|
380-420
|
A A A A A
|
A A A A A
|
A A A
|
|
PF-611
|
3
|
20-35
|
380-420
|
A A A A A
|
A A A A A
|
A A A
|
|
PF-612
|
3
|
20-35
|
380-420
|
A A A A A
|
A A A A A
|
A A A
|
|
Water based ceramic non-stick coating
|
|
C-104
|
1
|
30-45
|
280-300
|
A A A A A
|
A A A A
|
A A A A A
|
|
C-105
|
1
|
30-45
|
280-300
|
A A A A A
|
A A A A
|
A A A A A
|
|
C-106
|
2
|
34-50
|
280-300
|
A A A A A
|
A A A A
|
A A A A A
|
|
C-107
|
1
|
12-20
|
250-280
|
A A A A A
|
A A A A
|
A A A A A
|
|
C-108
|
2
|
34-50
|
280-300
|
A A A A A
|
A A A A
|
A A A A A
|
|
C-109
|
2
|
34-50
|
280-300
|
A A A A A
|
A A A A
|
A A A A A
|
|
Silicone resin non-stick coating
|
|
S-200
|
1
|
15-20
|
280-300
|
A A A A
|
A A A A A
|
A A A A
|
|
S-201
|
1
|
15-20
|
280-300
|
A A A A
|
A A A A A
|
A A A A A
|
|
S-202
|
1
|
15-20
|
280-300
|
A A A A
|
A A A A A
|
A A A A
|